Grinding Media

-           -          Hi-Alumina Bead

Product

Process

Components

Real Density

[g/cm³]

Bulk Density

[g/cm³]

Hardness

 [Mohs]

ACB58

Sintering

Al2O3:58%

SiO2 :42%

2.7

1.68

8

ACB92

Isostatic

Al2O3:92%

SiO2 :7.0%

3.6

2.2

8

Size [mm]

1.0-1.2mm, 5.0-80mm

Application:

ACB series are applicable in grinding and dispersing non-metal mineral powder (e.g. kaolin, calcium carbonate), coating, paint, and especially suitable for larger grinding equipment. We have improved the quality and performance of our beads on the basis of adopting strong point of domestic product of the same kind, thus making our product very competitive in terms of performance and price compared to either substituts (such as zirconia silicate beads and glass beads) or product of the same kind.

-           -          Zircon-Aluminum composite beads 

Product

Process

Components

Real Density

[g/cm³]

Bulk Density

[g/cm³]

Hardness

 [Mohs]

ZCB

Sintering

ZrO2;SiO2;Al2O3

3.2

2.0

8

Size [mm]

 1.0-1.2mm, 5.0-80mm

Application

 For wet grinding : Kaolin clay, Calcium carbonate, TiO2, Zirconium silicate, Ink, Pigments, Paints etc., industries.

 -          Zirconia Silicate beads (Fusion &Sintering process) 

Product

Process

Components

Real Density

[g/cm³]

Bulk Density

[g/cm³]

Hardness

 [Mohs]

ZSB-F

Fusion

ZrO268%;

SiO231%

3.86

2.3

7.2

ZSB-S

Sintering

ZrO268%;

SiO231%

4.0

2.5

8

Size [mm]

0.4-0.6, 0.6-0.8, 0.8-1.0, 1.0-1.2, 1.2-1.4, 1.4-1.6, 1.6-2.0, 2.0-2.5range can be customized.

Application

For wet grinding : Kaolin clay, Calcium carbonate, TiO2, Zirconium silicate, Ink, Pigments, Paints etc., industries.

 -          Yttrium Stablized Beads 

      ●ComponentZrO2 94.6%Y2O3  5.2±0.2%

      ●Real density:>6.0g/cm3

      ●Bulk density3.7-3.9g/cm3

      ●RigidityHRA 87, 9 (Mohs) 

      ●Slenderness ratio8.0Mpa.m1/2

      ●Crushing strength150kgf  2mm

      ●wearing value international standard

      ●Size(Diameter mm)0.6-0.80.8-1.01.0-1.21.2-1.41.4-1.7

          1.5-2.02.0-2.5345810 or to be customized

Yttrium Stablized Bead are produced with micron and sub-nanometer material by advanced technique, with all technical specifications and performance reaching international standards. Applicable in super-fine grinding and dispersing materials of high viscosity and rigidity, and materials requiring “zero contamination”, such as electric ceramic, magnetic material, zirconia, silica, zirconia silicate, titanium dioxide, medical food, pigment, dye, ink, and special chemical industry.

 -          Cerium-Stabilized beads

       ●Component  ZrO2+Ce > 80%

      ●Real density:>5.2g/cm3

      ●Bulk density3.3g/cm3

      ●RigidityHRA 87   9 (Mohs) 

      ●Slenderness ratio8.0Mpa.m1/2

      ●wearing value international standard

      ●Specifications(Diameter mm)0.6-0.80.8-1.01.0-1.21.2-1.41.4-1.7

          1.5-2.02.0-2.53456mm or to be customized

Cerium-Stabilized beads are produced with micron and sub-nanometer material by

advanced technique, with all technical specifications and performance reaching

international standards. Applicable in super-fine grinding and dispersing materials

of high viscosity and rigidity, and materials requiring “zero contamination”, such

as electric ceramic, magnetic material, zirconia, silica, zirconia silicate, titanium

dioxide, medical food, pigment, dye, ink, and special chemical industry.

-          Ceramic shot blasting media

Product

Process

Components

Real Density

[g/cm³]

Bulk Density

[g/cm³]

Vickers Hardness

 [HV1]

SBB

Shot blasting beads

Electro-fusing

ZrO2 68%

SiO2 32%

3.85

2.3

700

Specification

[mm]

JZB20:    0.600-0.850mm,  JZB30 : 0.425-0.600mm

JZB40:    0.250-0.425mm,  JZB60:  0.125-0.250mm

JZB120:  0.063-0.125mm,  JZB125:0.000-0.125mm,

JZB205 : 0.000-0.063mm

JZ100:    0.100-0.150mm,    JZ150: 0.150-0.210mm,  

JZ210:    0.210-0.300mm     JZ300: 0.300-0.425mm,  

JZ425:    0.425-0.600mm,    JZ600: 0.600-0.850mm

JZ850:    0.850-1.180mm

Application

Used for surface treatment: Shot blasting, shot peening in automotive, aircraft, shipbuilding, industries.

 -          Hybrid Ceramic Beads 

Item

Unit

Si3N4

ZrO2

SiC

Al2O3

Materials

-

Sintered Si3N4

ZrO2

Sintered SiC

99.5%Al2O3

Density

g/cm³

3.2

6.0

3.15

3.95

Color

-

Black, Grey

White

Black

White, Ivory

Young’s Modulus

Gpa

300-320

210

350

380

Hardness

Hv

1400-1700

1100-1300

2000-2500

1800

HRC

75-80

70-50

85-90

80

Bending Strength

MPa

800-1200

950-1200

400-500

300-500

Fracture toughness

Mpam½

5.0-7.0

8.0-10.0

3.0-4.0

3.0-4.0

Max.Working Temperature

800

400

1300

1000

 

 

 

 

 

 

 

 

 

 

 

 

 

-          Ceramic Structural Parts 

Physical properties

Unit

95 ALU

99 ALU

Application

Porosity

%

0

0

Welding nozzles,

Chemical seal faces, Thread guides, Ceramic ferrules; It could be manufactured in various shapes and sizes & various surface finish

 

Density

g/cm³

3.65

3.85

Hardness

HRA

85

90

Flexural Strength

Mpa

300

350

Compressive Strength

Mpa

2500

2800

Tensile Strength 25

Mpa

160

240

Linear Expansion Coefficient

mm/, [25-300]

6.2*10-6

 

Dielectric constant at 25

ε,1 MHz [20]

9.0

9.2

Dielectric Strength

Kv/mm

20

20

Safe Use Temperature

1500

1700

Volume Resistance

Ω.cm [25]

1014

1014

Water Absorption

%

0

0

Barite
-Natural Barite Ore
     -Natural Barite Ore
-Natural Barite Powder
     -Drilling Grade Powder
     -Chemical Grade Powder
     -Paint Grade Powder
Primary Chemicals
-Acid
-Ammonium Chemicals
-Barium Chemicals
-Magnesium Chemicals
-Phosphate Chemcials
-Sodium Chemicals
-Strontium Chemicals
-Zinc Chemicals
-Zirconium Chemicals
-Grinding Media
Industrial Minerals
-Alumina
-Bauxite, Flint Clay, Mullite
-Magnesia
-Talc
-Titanium Dioxide
-Titanium Slag
-Graphite